E380-16 Welding Electrode: High-Performance Cr19Ni10 Stainless Steel Electrode for Superior Welding

PRODUCTS


Home > Products > Welding Electrode > E308-16 Welding Electrode

PRODUCT CATEGORY

CONTACT US

E308-16 Welding Electrode

1.Qualified tensile strength and hardness

2.Approved by ISO9001, CE, SGS, BV, Form-E, CO , MTC Certificates

3. Quick delivery and standard wooden exporting package.

4. Low MOQ and Flexible Production Ability.

5.Support payment with T/T, L/C , paypal, kunlun bank, etc.

6. OEM and ODM, welcome customers to visit our factory for better understanding;

7. Our factory provide steel products with competitive price and reliable quality;

8. Value friendship and trustworthy, devote to provide long-term service to our distinguished customers.

+8613222808717

+86 13222808717

Darren@screwmetal.com

Chemical composition of deposited metal

project	C	Cr	Ni	Mo	Mn	Si	P	S	Cu
Guaranteed value	≤0.08	18.0-21.0	9.0-11.0	≤0.75	0.5-2.5	≤1.00	≤0.04	≤0.03	≤0.75
Example	0.06	19.86	9.35	0.09	0.96	0.78	0.028	0.010	0.08

Mechanical properties of deposited metal

project	tensile strengthRm/MPa	ElongationA（%）
Guaranteed value	≥550	≥30
Example	600	40

Reference current

Welding diameter（mm）	Φ2.5	Φ3.2	Φ4.0	Φ5.0
Welding length(mm)	300	350	400	400
Welding current（A）	60~85	85~120	115~160	160~200

Features:

A102 is a Cr19Ni10 stainless steel electrode with calcium titanium coating. The deposited metal has good mechanical properties and resistance to intergranular corrosion. It has excellent welding process performance and anti-pore performance, and the coating is resistant to redness and cracking. Can be used for both AC and DC.

Notes:

1. The electrode must be baked at about 300-350℃ for 1 hour before welding.

2. Rust, oil, moisture and other impurities on the weldment must be removed before welding.

3. It is recommended to use a DC power supply. The current should not be too large to avoid redness and cracking of the drug skin.

Get a Free Quote